Material: | PFA |
---|---|
Kind: | Plastic Bar |
Water Absorption: | <0.01% |
Contraction Percentage: | <0.4% |
Tensile Strength: | 25-35 MPa |
Density: | 2.1-2.2 g/cm3 |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
- PFA Welding Rod - Meanwhile, It has better thermoplastic properties. This PFA welding rod is made of imported ultra-pure PFA resin by extrusion process. It is mainly used for welding PTFE sheet and PTFE tubes to against corrosion, proofing, bonding and etc.
PFA (commonly known as the soluble PTFE), it basically retained the properties of PTFE. Such as: Outstanding high & low temperature resistance, chemical stability, electrical insulation, self-lubricating, non-sticky and high mechanical strength properties, the outstanding characteristic is with good folding and cracking resistance, and the mechanical strength is 1.6 times of PTFE or more.
Features: Transparent color and smooth surface
Welding current:220(A) Low and high temperature resistance,
long term service temperature:-80~+260ºC Universal chemical and corrosion resistance
Exceptional thermal stress-crack resistance Excellent electrical properties Outstanding fire resistance Good hot melting
sealing and weldability
Property | Norm | Value |
Density(g/cm³) | ISO1183 | 2.1~2.2 |
Tensile Strength at Break(Mpa) | ISO527 | 25-35 |
Modulus of Elasticity(Gpa) | ISO527 | 0.4-0.5 |
Elongation at break(%) | ISO527 | 200-380 |
Hardness Shore(Shore D) | Durometer | 60 |
Temperature Range(°C) | / | -196-260 |
Coefficient of Linear Thermal Expansion(10-4/°C) | ISO11359 | 1.2 |