| Material: | PTFE |
|---|---|
| Usage: | Engineering Plastics |
| Plastic Forming Method: | Mould Compression |
| Color: | White |
| Density: | 2.10-2.g/cm3 |
| Tensile Strength: | 15mpa |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier PTFE (king of plastic) is the most commonly used fluoroplastic. Also with widest applications. PTFE has excellent corrosion resistance, aging resistance, high & low temperature resistance, good lubrication and insulation, non-sticky, harmless. It is widely used in the industries like aviation, chemical, electronics, bridge, mechanical manufacturing, textile, papermaking and ceramics etc.
1) Molded PTFE rod ( Dia. 20mm-Dia. 380mm); Extruded PTFE rod ( Dia. 2mm-Dia. 150mm )
2). PTFE skive Sheet (0.5-5mm thickness, special size can be customized)
3). Molded PTFE sheet(1-80 thickness, 100-2000mm width; 100-2000mm length
4). Molded PTFE sheet (1-65mm thickness; Dia. 100-1000mm)
5). Full size for molded PTFE tube, extruded PTFE tube
6). Modified PTFE products ( fill with glass fibre, graphite, carbon etc. )
7). PTFE machined parts.
1. Very low coefficient of friction
2. Highly inert
3. High melting point
4. Wonderful electrical properties.
| Property | Norm | Value |
| Density(g/cm³) | ISO1183 | 1.8~2.5 |
| Tensile Strength at Break(Mpa) | ISO527 | 18~30 |
| Modulus of Elasticity(Gpa) | ISO527 | 0.35~0.5 |
| Elongation at break(%) | ISO527 | 150~350 |
| Hardness Shore(Shore D) | Durometer | 50~65 |
| Temperature Range(°C) | / | -196~260 |
| Coefficient of Linear Thermal Expansion(10-4/°C) | ISO11359 | 1.0 |
• Full traceability on all material under ISO 9001:2015
• Reliable and brand raw material
• In-house tensile strength and elongation testing
• Hot size on stock and quick lead time
• With over 20 years of manufacture experience of fluoropolymers